LG Chemical LUMID HI3232A(W) PA6+MF23%, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI3232A(W) PA6+MF23%, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+MF23%, High ImpactApplication: Automotive PartsCAS No. 25038-54-4, 9010-79-1 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.013 cm/cm @Thickness 3.20 mm |
0.0090 - 0.013 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 12 % @Thickness 3.20 mm |
12 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.92 GPa @Thickness 3.20 mm |
569 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 1.00 mm |
559 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Front Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Polymer Resources TP-G15 Polybutylene Terephthalate, 15% Glass Reinforced
- PolyOne Geon™ Vinyl Flexible C90A0 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP Lubricomp DEL34 PC (Europe-Africa-Middle East)
- Fainplast Compounds RE 325/2 Rigid PVC, Extrusion
- Solvay Chemicals Blanc fixe HD 80
- A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
- Wellman Wellpet® PR118-N2 Unfilled Polyester PET
- Formosa Plastics Formolene® 4100T Injection Molding Polypropylene
- 3M AC-770 Class B-1 Aerospace Sealant
- Arlon R32481R014 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved