- Polymer Property : Flexural Yield Strength = 98.1 MPa
Polymer Property : Flexural Yield Strength = 98.1 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| LG Chemical LUCON CP6052 PC/ABS+CNT Description Injection Molding Grade, PC/ABS+CNT, Electrostatic Dissipation, Low Surface Resistivity, Improved Impact StrengthApplication: Laser diode Tray, ATM parts, Telecommunication Station Housi.. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| LG Chemical LUCON CP6062EX PC/ABS+CNT Description: Sheet Extrusion or Injection Molding, PC/ABS+CNT, Electrostatic Dissipation, Wide Processing Range, Low Surface ResistivityApplication: BLU Carrying TrayCAS No. 103598-77-2, 9003-56-9, .. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| LG Chemical LUCON PS4200 ABS+CF Description: Injection Molding, ABS+CF, Electrostatic Dissipation, Good Dimensional Stability, Low WarpageApplication: IC TrayCAS No. 9003-56-9, 12001-26-2 and 7440-44-0Information provided by LG Ch.. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN177N Nylon Extrusion Resin Excellent transparent & flexible copolyamide, typical applications are fishing nets & fishing linesInformation provided by US distributor, API-Kolon. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOL GP2200 PP+GF20% Description: Injection Molding, PP+GF20%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® GP2056F PBT+GF5% Description: Injection Molding, PBT+GF5%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 71342-77-3, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GN5001RFP PC/ABS, Halogen Free Flame Retardant, Heat Resistance Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, General PurposeApplication: E&E (TV, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Ch.. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1000HU PC, Transparent Description: Injection Molding, PC, General Purpose, Transparency, UV StabilityApplication: Electric & Electronic (Housing, Components) For Suit caseCAS: 103598-77-2Information provided by LG Chemic.. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN173MC M/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| LG Chemical GPPS 25SP(I) PS, High Transparency, Heat Resistance Description: Injection Molding, PS, High Transparency, Heat ResistanceApplication: PSP, Food Tray, Electric/Electrical Component, CoatingCAS: 9003-53-6Information provided by LG Chemical |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1000LS PC, Transparent Description: Injection Molding, PC, General Purpose, Transparency, High FlowApplication: IT/OA, Electric & Electronic Housing and Components, Automotive InteriorCAS: 103598-77-2Information provided .. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1000M PC, Transparent Description: Injection Molding, PC, General Purpose, TransparencyApplication: IT/OA, Electric & Electronic Housing and Components, Automotive Exterior and InteriorCAS: 103598-77-2Information provide.. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1006FM PC, Flame Retardant Description: Injection Molding, PC, Flame RetardantApplication: IT/OA, E&E Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® P305G20 PP, 20% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Tribit® 1500G10 PBT, Reinforced General Purpose Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1500G10 is a reinforced, general purpose gr.. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Trirex® 3025GN10 Polycarbonate, Reinforced Flame Retardancy PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025GN10 is a reinforced flame retardant grade.Applications: LCD Panel Frame (dimensio.. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Trirex® 3025GRU10 Polycarbonate, 10% Glass Reinforced TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Trirex® DMH3000S Polycarbonate, High Flow Flame Retardancy PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.DMH3000S is a high flow, flame retardant grade.Applications: LCD TV Front cover, high .. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® P305G20 PP, 20% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS 2000 SAN Resin Clear SANInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS1000 Sparkle SAN Resin High Transparent SANInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS 2000 SAN Resin Clear SANInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS1000M SAN Resin Clear SAN, Pen barrel applicationInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS 2000 Glitter SAN Resin High Transparent SANInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS1000 SAN Resin Clear SANInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMGS20 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Triloy® S460G15 Polymer Alloy, Reinforced Excellent impact, formability and weather resistance.220 is a reinforced grade.Applications: LCD Panel Frame - for dimensional stabilityInformation provided by Samyang. |
|||
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Samyang Trirex® 3025GRU30 Polycarbonate, 30% Glass Reinforced TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electr.. |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1000ML PC, Transparent Description: Injection Molding, PC, General Purpose, TransparencyApplication: IT/OA Housing and Components, Automotive InteriorCAS: 103598-77-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Santron IMS1000 Sparkle SAN Resin High Transparent SANInformation provided by Bhansali |
|||