- Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing
Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behaviour, self-lubricating, for highest tribologic needs.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 75.0 MPa | 10900 psi | |
| Elongation at Yield | 3.3 % | 3.3 % | |
| 4.4 % | 4.4 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 105 MPa | 15200 psi | |
| Flexural Modulus | 3.40 GPa | 493 ksi | |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C | 27.8 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | graphite grey |
Users viewing this material also viewed the following:
- MV Labs AS600 AsI3 Arsenic(III) iodide
- Quadrant EPP Symalit® ECTFE Ethylene-Chlorotrifluoroethylene (ASTM Product Data Sheet)
- Resinlab® RC8048 Anaerobic Retaining Compound
- Lord Adhesives 506 Semi-Flexible, Medium Cure, Medium Viscosity Acrylic Adhesive
- Taiwan Sheen Soon Sheenthane® A9313H Thermoplastic Polyurethane Elastomer
- Total Lumicene® mPE M6040 S01 Metallocene Polyethylene, Cast Film
- A. Schulman PP 3471-01 Polypropylene High Flow Homopolymer Polypropylene
- Hexcel® Redux® 312/5 Modified epoxy film adhesive
- China Tungsten STG60-15 PM Structural Parts
- 3M 32666 Tan Heavy Duty Performance Coating - Part B
Copyright © lookpolymers.com All Rights Reserved