LG Chemical LUMID HI1102B(W) PA66, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI1102B(W) PA66, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding,PA66, High ImpactApplication: Automotive (Covers)CAS No. 32131-17-2 and 9010-79-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.20 mm |
0.012 - 0.016 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 40 % @Thickness 3.20 mm |
40 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 79.4 MPa @Thickness 3.20 mm |
11500 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 3.20 mm |
313 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.67 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C @Thickness 6.40 mm |
437 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 6.40 mm |
158 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 1.00 mm |
610 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | Injection Molding |
| Front Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4970 TPE, Transparent
- SABIC Innovative Plastics Cycolac® FR15U ABS
- Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced
- Honeywell Spectra® 1000 Fiber
- M. Holland Company SA311 Styrene Acrylonitrile
- Karina 828-08/20-AY-ERYB-PO Beige PVC Compound
- Solvay ALKAMULS® S 80 Surfactant
- Trelleborg E450 EPDM Rubber
- DSM Akulon® S223-D Nylon 66 (European Grade) (Dry)
- ATI Allvac® Vasco® 317 L UNS S31703 Specialty Steel
Copyright © lookpolymers.com All Rights Reserved