LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6, Medium ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 130 % @Thickness 3.20 mm |
130 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.65 GPa @Thickness 3.20 mm |
384 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 6.40 mm |
338 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 1.00 mm |
483 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 195 sec | 195 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Nozzle Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Nylene® Norpex® AX20MRFR , 20% Mineral Reinforced, Flame Retardant Polyphenylene Ether
- LG Chemical LUMID GN-2251BF Flame Retardant PA Alloy
- Indium Corp. Indalloy® 261 Bismuth-Silver Solder Alloy
- Unifrax Fiberfrax® 6001-F-5 Kaolin Bulk Fiber
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Polyram PlusTek RA314G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized
- Hexcel® HexPly® F522 Epoxy Resin, F3C433 Carbon Fabric
- ExxonMobil Solvesso™ Aromatic 150 Aromatic Fluid
- Ashley Polymers Ashlene® P123WO PBT Polyester, 15% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved