ExxonMobil Label-Lyte™ 29LL210 Preliminary Data Sheet OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 29LL210 Preliminary Data Sheet OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A biaxially oriented, transparent polypropylene film for pressure sensitive labeling and tape applications.Availability: Africa & Middle East and EuropeKey Features: High yieldGood gloss transparencyGood moisture resistanceGood printability on the treated side and receptivity to laminating adhesivesExcellent machine performanceRecommended for in-line top coating Applications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsDry Foods and Beverage Powders Uses: Reel-Fed LabelsProcessing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing, UV Flexographic Printing, UV Offset Lithography Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 27.9 microns | 1.10 mil | ExxonMobil Method |
| Coating Weight | 25.9 g/m² | 16.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.60 GPa | 522 ksi | TD; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.5 % @Temperature 135 °C, Time 432 sec |
6.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 4.5 % @Temperature 135 °C, Time 432 sec |
4.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 26600 in2/lb |
Users viewing this material also viewed the following:
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Carbon Black Filled
- Reliance Industries Repol B030MG Polypropylene
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 17% Plasticizer (discontinued **)
- ITW Plexus Plexusâ„¢ MA1020 Methacrylate Adhesive
- Heatbath/Park Parquench 60 Water-Based Quenchant
- Dow Corning SYL-OFF® PMCP7137 High Speed Crosslinker
- Hippe PF CC 32 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Arlon AD260A PTFE/Woven Fiberglass/Microdispersed Ceramic Filled Laminate for RF & Microwave PCBs
- ArcelorMittal H 220 Solid solution steel, Cold rolled
- Unipetrol PND 33-352-94 Extra Light Fuel Oil
Copyright © lookpolymers.com All Rights Reserved