Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.37 - 1.65 g/cc
0.0495 - 0.0596 lb/in³
Average value: 1.53 g/cc Grade Count:11
Filler Content 30.0 - 40.0 %
30.0 - 40.0 %
Average value: 32.0 % Grade Count:5
Water Absorption 0.0500 - 0.200 %
0.0500 - 0.200 %
Average value: 0.122 % Grade Count:10
Viscosity 60000 - 650000 cP

@Temperature 400 - 400 °C
60000 - 650000 cP

@Temperature 752 - 752 °F
Average value: 396000 cP Grade Count:5
60000 - 650000 cP

@Shear Rate 1000 - 1000 1/s
60000 - 650000 cP

@Shear Rate 1000 - 1000 1/s
Average value: 396000 cP Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00327 cm/cm Grade Count:11
Linear Mold Shrinkage, Transverse 0.00500 - 0.0150 cm/cm
0.00500 - 0.0150 in/in
Average value: 0.00940 cm/cm Grade Count:10
Melt Flow 2.00 - 15.0 g/10 min
2.00 - 15.0 g/10 min
Average value: 8.40 g/10 min Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 105
100 - 105
Average value: 102 Grade Count:5
Tensile Strength, Ultimate 110 - 191 MPa
16000 - 27700 psi
Average value: 156 MPa Grade Count:11
50.0 - 205 MPa

@Temperature -50.0 - 250 °C
7250 - 29700 psi

@Temperature -58.0 - 482 °F
Average value: 124 MPa Grade Count:1
Tensile Strength, Yield 158 - 188 MPa
22900 - 27300 psi
Average value: 168 MPa Grade Count:4
Elongation at Break 1.80 - 3.20 %
1.80 - 3.20 %
Average value: 2.53 % Grade Count:10
Modulus of Elasticity 6.20 - 16.7 GPa
899 - 2420 ksi
Average value: 11.1 GPa Grade Count:11
Flexural Yield Strength 160 - 283 MPa
23200 - 41000 psi
Average value: 235 MPa Grade Count:11
54.0 - 54.0 MPa

@Temperature 250 - 250 °C
7830 - 7830 psi

@Temperature 482 - 482 °F
Average value: 54.0 MPa Grade Count:1
Flexural Modulus 5.50 - 15.4 GPa
798 - 2230 ksi
Average value: 10.0 GPa Grade Count:11
Compressive Yield Strength 139 - 182 MPa
20200 - 26400 psi
Average value: 162 MPa Grade Count:5
Shear Strength 80.8 - 89.0 MPa
11700 - 12900 psi
Average value: 84.3 MPa Grade Count:5
Izod Impact, Notched 0.500 - 1.20 J/cm
0.937 - 2.25 ft-lb/in
Average value: 0.858 J/cm Grade Count:10
Izod Impact, Unnotched 4.30 - 10.0 J/cm
8.06 - 18.7 ft-lb/in
Average value: 7.86 J/cm Grade Count:10
Izod Impact, Notched (ISO) 8.50 - 14.0 kJ/m²
4.04 - 6.66 ft-lb/in²
Average value: 11.9 kJ/m² Grade Count:4
Izod Impact, Unnotched (ISO) 41.0 - 70.0 kJ/m²
19.5 - 33.3 ft-lb/in²
Average value: 61.0 kJ/m² Grade Count:4
K (wear) Factor 10100 x 10-8 mm³/N-M
5000 x 10-10 in³-min/ft-lb-hr
Average value: 10100 x 10<sup>-8</sup> mm³/N-M Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 15.0 - 19.0 µm/m-°C
8.33 - 10.6 µin/in-°F
Average value: 17.0 µm/m-°C Grade Count:4
Specific Heat Capacity 1.26 - 1.70 J/g-°C

@Temperature 50.0 - 200 °C
0.301 - 0.406 BTU/lb-°F

@Temperature 122 - 392 °F
Average value: 1.47 J/g-°C Grade Count:5
Thermal Conductivity 0.280 - 0.310 W/m-K
1.94 - 2.15 BTU-in/hr-ft²-°F
Average value: 0.294 W/m-K Grade Count:5
Melting Point 340 - 372 °C
644 - 702 °F
Average value: 347 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 209 - 360 °C
408 - 680 °F
Average value: 268 °C Grade Count:10
Glass Transition Temp, Tg 150 - 158 °C
302 - 316 °F
Average value: 156 °C Grade Count:6
Flammability, UL94 V-1 - V-0
V-1 - V-0
Grade Count:9
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 - 2.10e+17 ohm-cm
1.00e+16 - 2.10e+17 ohm-cm
Average value: 9.11e+16 ohm-cm Grade Count:9
Surface Resistance 1.00e+16 - 1.90e+17 ohm
1.00e+16 - 1.90e+17 ohm
Average value: 1.54e+17 ohm Grade Count:5
Dielectric Constant 3.48 - 3.74
3.48 - 3.74
Average value: 3.62 Grade Count:5
Dielectric Strength 14.0 - 19.0 kV/mm
356 - 483 kV/in
Average value: 15.7 kV/mm Grade Count:10
Dissipation Factor 0.000 - 0.00600
0.000 - 0.00600
Average value: 0.00243 Grade Count:5
Processing Properties Metric English Comments
Nozzle Temperature 360 - 425 °C
680 - 797 °F
Average value: 387 °C Grade Count:6
Melt Temperature 360 - 404 °C
680 - 759 °F
Average value: 374 °C Grade Count:6
Mold Temperature 149 - 220 °C
300 - 428 °F
Average value: 181 °C Grade Count:7
Drying Temperature 149 - 175 °C
300 - 347 °F
Average value: 151 °C Grade Count:7