LG Chemical LUMAX GP5106FI PBT+ABS+GF10%, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant
Manufacturer LG Chemical
Trade Name LUMAX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMAX GP5106FI PBT+ABS+GF10%, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding Grade, PBT+ABS+GF10%, Flame Retardant, Impact Modified, Dimensional StabilityApplication: E&E (Switch)CAS: 9003-56-9, 68928-70-1, 65997-17-3, 24968-12-5, 9003-54-7 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0090 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0090 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.9 MPa

@Thickness 3.20 mm
 8110 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 83.4 MPa

@Thickness 3.20 mm
 12100 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 2.94 GPa

@Thickness 3.20 mm
 427 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.10 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
Peak at Break
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 6.40 mm
 230 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm
 660 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 175 V
175 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=3.00 mm
 30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 3.00 mm
 30 - 60 arcs

@Thickness 0.118 in
60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 225 - 235 °C
437 - 455 °F
Injection Molding
Middle Barrel Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Front Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Nozzle Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Melt Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 100 °C
212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding