- LG Chemical HI121U ABS
LG Chemical HI121U ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical HI121U ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, Well Balanced Mechanical Properties, Good weatherabilityApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 22 g/10 min @Load 10.0 kg, Temperature 220 °C |
22 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 46.1 MPa @Thickness 3.20 mm |
6680 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 75.5 MPa @Thickness 3.20 mm |
11000 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.60 GPa @Thickness 3.20 mm |
377 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
5.51 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- DSM Akulon® K224-PG2U (Cond.) 13% Glass Reinforced, Impact Modified Nylon 6 (North America) (discontinued **)
- Lehmann & Voss LUVOCOM® 80/CF/10/BK Polyacetal-copolymer, with carbon fiber
- LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
- Lubriplate Rock Drill Oil Specialty Oil 10R and Fluid
- SABIC Innovative Plastics Xenoy® X6800BM PBT (Asia Pacific)
- Dow Corning MG 7-9850 SOFT SKIN ADHESIVE KIT (A&B)
- Chosun Refractories APC-50G Acid-proof Castable
- Eurostar Star L PA6 D83 PA6, Injection Molded
Copyright © lookpolymers.com All Rights Reserved