SABIC Innovative Plastics LNP Stat-kon REL36 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon REL36 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* REL36 is a compound based on Nylon 6/6 containing carbon fiber and PTFE. Characteristics of this grade are Statically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.394 g/cc | 0.05036 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.75 % | 0.75 % | 23°C / 50% RH; ISO 62 |
| 0.52 % @Time 86400 sec |
0.52 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0017 cm/cm @Time 86400 sec |
0.0015 - 0.0017 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0080 cm/cm @Time 86400 sec |
0.0010 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 154 MPa | 22300 psi | Type I, 5 mm/min; ASTM D 638 |
| 175 MPa | 25400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 154 MPa | 22300 psi | Type I, 5 mm/min; ASTM D 638 |
| 173 MPa | 25100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D 638 |
| 1.3 % | 1.3 % | 5 mm/min; ISO 527 | |
| 181.7 % | 181.7 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D 638 |
| 1.2 % | 1.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 24.61 GPa | 3569 ksi | 1 mm/min; ISO 527 |
| 32.44 GPa | 4705 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 302 MPa | 43800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 16.18 GPa | 2347 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 17.35 GPa | 2516 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.69 J/cm @Temperature 23.0 °C |
10.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² @Temperature 23.0 °C |
19.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 78.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 5.0 ohm | 2.0 - 5.0 ohm | ASTM D 257 |