Kingfa MAC-601 PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa MAC-601 PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic partsComputer and accessoriesHousehold appliance thin wall partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc

@Temperature 23.0 °C
1.14 g/cc

@Temperature 73.4 °F
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Temperature 23.0 °C
0.0050 - 0.0070 in/in

@Temperature 73.4 °F
ASTM D955
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break >= 50.0 MPa
>= 7250 psi
50mm/min; ASTM D638
Elongation at Break >= 60 %
>= 60 %
50mm/min; ASTM D638
Flexural Strength 82.0 MPa
11900 psi
2mm/min; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
2mm/min; ASTM D790
Izod Impact, Notched 5.50 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
10.3 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm,
Temperature 23.0 °C
NB

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 124 °C

@Thickness 6.40 mm
255 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 106 °C

@Thickness 6.40 mm
223 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Dielectric Strength 30.0 kV/mm
762 kV/in
1.6mm; ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 265 °C
<= 509 °F
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Start Point: 240°C
Middle Barrel Temperature 230 - 250 °C
446 - 482 °F
Start Point: 245°C
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Start Point: 250°C
Melt Temperature 220 - 250 °C
428 - 482 °F
Start Point: 245°C
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Start Point: 70°C
Drying Temperature 100 - 110 °C

@Time 14400 - 21600 sec
212 - 230 °F

@Time 4.00 - 6.00 hour
Pre-dry
Back Pressure 0.300 - 1.00 MPa
43.5 - 145 psi
Descriptive Properties Value Comments
Injection Speed 60-90%