Kingfa PBT-RG002 Flame Retardant PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PBT-RG002 Flame Retardant PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Flame retardantGood chemical resistanceOutstanding surfaceEasy processingHigh impactApplications:Injection moldingConnectors, terminal blocksRelay, switchBobbinsPlugsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc @Temperature 23.0 °C |
1.32 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.040 % @Temperature 23.0 °C, Time 86400 sec |
0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Temperature 23.0 °C |
0.011 - 0.016 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 10mm/min; ASTM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 5.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.55 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 6.40 mm |
178 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.700 mm |
V-0 @Thickness 0.0276 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 265 °C | <= 509 °F | |
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 235°C |
| Middle Barrel Temperature | 230 - 255 °C | 446 - 491 °F | Start Point: 245°C |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 255°C |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Start Point: 60°C |
| Drying Temperature | 120 - 140 °C @Time 14400 - 21600 sec |
248 - 284 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate to High |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® HPV UHMW-PE (ASTM Product Data Sheet)
- Cookson Group Plaskon® ULS-12LA Molding Compound (discontinued **)
- LG Chemical 80HFICELLHK SAN, High Transparency, Heat Resistance, Chemical Resistance
- Gouda Vuurvast CURON 160 H Dense Refractory Castable
- Solvay TECHNYL® B 218 V30 Black 21 N PA66, 30% glass fiber, DRY
- SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Wingate Alloys Winco XR Special High Strength Alloy Wear Bar
- Dow Corning SYL-OFF® PMCP7367 Crosslinker
- Diamond Polymers NPP25-1202 TF20 20% Talc Filled Copolymer Polypropylene, Impact Modified, High Heat, High Stiffness with UV and Paintable Versions
Copyright © lookpolymers.com All Rights Reserved