Eurostar Staramide BG4 PA6, 20% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BG4 PA6, 20% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BG4 is a 20% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 1.40 %

@Temperature 23.0 °C
1.40 %

@Temperature 73.4 °F
50% RH; ISO 62
Water Absorption at Saturation 6.8 %

@Temperature 23.0 °C
6.8 %

@Temperature 73.4 °F
ISO 62-1
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Hardness, Rockwell L 123
123
ISO 2039-2
Tensile Strength at Break 145 MPa
21000 psi
5 mm/min; ISO 527
Elongation at Break 3.8 %
3.8 %
5 mm/min; ISO 527
Tensile Modulus 6.50 GPa
943 ksi
1 mm/min; ISO 527
Flexural Strength 200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -40.0 °C
2.86 ft-lb/in²

@Temperature -40.0 °F
80x10x4; ISO 180/1A
7.00 kJ/m²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
80x10x4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1A
8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1U
50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1U
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
5.50 J/cm²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 20

@Load 1.00 kg
20

@Load 2.20 lb
CS-17; E2P Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
19.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
52.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
388 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 206 °C
403 °F
B/120; ISO 306
208 °C
406 °F
B/50; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
Oxygen Index 24 %
24 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 50.0 - 60.0 Hz
3.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
508 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0061

@Frequency 50.0 - 60.0 Hz
0.0061

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.016

@Frequency 1.00e+6 Hz
0.016

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 400 V
400 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Zone 1
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 2
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Zone 3
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %