BASF Ultramid® 8254 HS BK-102 PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 8254 HS BK-102 PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 8254 HS is a highly flexible, heat stabilized, impact modified nylon 6 extrusion grade for tubing applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | dry; ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | 24 hour; ISO Test |
| 7.1 % | 7.1 % | beginning dry; ISO 62 | |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527 |
| 26.0 MPa | 3770 psi | 2 in/min; ASTM Test | |
| 104 MPa @Temperature -40.0 °C |
15100 psi @Temperature -40.0 °F |
ISO Data | |
| 104 MPa @Temperature -40.0 °C |
15100 psi @Temperature -40.0 °F |
ASTM Test | |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 30 % | 30 % | 50mm/min; ISO 527 |
| Tensile Modulus | 0.460 GPa | 66.7 ksi | 1mm/min; ISO 527 |
| 0.145 GPa @Temperature 120 °C |
21.0 ksi @Temperature 248 °F |
ISO Data | |
| 0.230 GPa @Temperature 80.0 °C |
33.4 ksi @Temperature 176 °F |
ISO Data | |
| 3.00 GPa @Temperature -40.0 °C |
435 ksi @Temperature -40.0 °F |
ISO Data |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Injection molding |
| Mold Temperature | 70.0 °C | 158 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK-102 | |
| Commercial Status | Active America | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Extrusion | |
| Processing | Injection Molding | |
| Other Extrusion | ||
| Profile Extrusion | ||
| Special characteristic | Heat stabilized or stable to heat | |
| UL.UL-C | Yes |
Users viewing this material also viewed the following:
- Proto3000 Accura® 45HC Plastic Stereolithography (SLA) Prototyping Polymer
- BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Glastic GoldMemberâ„¢ Pre-tensioned Fiber Reinforcements
- Borealis RJ900MO Polypropylene Random Copolymer
- Polyram Polytron P60B08-S Polypropylene, 60% Long Glass Fiber
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- Daikin POLYFLON M-392 PTFE Molding Powder, Free Flow
- ConocoPhillips Hydroclear® 68 Rock Oil
- ExxonMobil Escorene™ FL 00218 Ethylene Vinyl Acetate Copolymer (European Grade)
Copyright © lookpolymers.com All Rights Reserved