Eurostar Staramide AST42K PA66, Impact Modified, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide AST42K PA66, Impact Modified, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AST42K is a Low Temperature Impact Modified Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.015 - 0.020 cm/cm
0.015 - 0.020 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 20 %
20 %
5 mm/min; ISO 527
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -40.0 °C
 4.28 ft-lb/in²

@Temperature -40.0 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
11.0 kJ/m²

@Temperature -20.0 °C
 5.23 ft-lb/in²

@Temperature -4.00 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 92.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 51.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 220 °C
428 °F
B/50; ISO 306
225 °C
437 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 1
Middle Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 2
Front Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 3
Melt Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %