BASF Ultramid® A3W PA66 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3W PA66 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Free-flowing, heat aging resistant and rapidly processable grade for technical parts subject to high stress such as bearings and bearing cages, gearwheels and spool bodies.Information provided by BASF
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 8.0 - 9.0 %
8.0 - 9.0 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.5 - 3.1 %
2.5 - 3.1 %
23°C; 50% RH; ISO 62
Viscosity Measurement 150
150
ISO 307
Linear Mold Shrinkage 0.0085 cm/cm
0.0085 in/in
restricted
Melt Flow 113 g/10 min

@Load 5.00 kg,
Temperature 275 °C
113 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 20 %
20 %
50mm/min; ISO 527-1/-2
Modulus of Elasticity 1.10 GPa
160 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Specific Heat Capacity 1.70 J/g-°C
0.406 BTU/lb-°F
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 260 °C
500 °F
DIN 53765
Maximum Service Temperature, Air 121 °C
250 °F
for 50% loss of tensile strength after 20000hr
147 °C
297 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm
1.00e+9 ohm-cm
IEC 60093
Surface Resistance 1.00e+9 ohm
1.00e+9 ohm
IEC 60093
Dielectric Constant 5.0

@Frequency 1.00 Hz
5.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.20

@Frequency 1.00e+6 Hz
0.20

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 500 V
500 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe