- Solvay Technyl® C216V25 25% Glass Filled Nylon 6
Solvay Technyl® C216V25 25% Glass Filled Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C216V25 25% Glass Filled Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183-A |
| Water Absorption | 1.0 % | 1.0 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 162 MPa | 23500 psi | ISO 527 |
| Elongation at Break | 3.9 % | 3.9 % | ISO 527 |
| Tensile Modulus | 8.41 GPa | 1220 ksi | ISO 527 |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Compression Zone |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Nozzle Temperature | 241 - 260 °C | 465 - 500 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ ATH-XC-361E Acetal (POM) Homopolymer
- Nylene® Vexel™ B12GF30 , 30% Glass Reinforced PBT
- Kraton® G1650 + PPE blend (10/90)
- Latrobe TNWâ„¢ ASTM M10 High Speed Steel
- A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
- ChevronTexaco HDAX® SAE 30 Ashless Gas Engine Oil
- CMW® ELKALOY D Copper Alloy, Aluminum Bronze
- Cossa Polimeri ESTABLEND PA 2516 GF ABS / Nylon 6 Blend, 8% Glass Filled
- Arkema Group Pebax® 7233 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- CeramTec ATZ Alumina Toughened Zirconia, Dental Grade
Copyright © lookpolymers.com All Rights Reserved