BASF Procom® D 1175 Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Procom® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Procom® D 1175 Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
| Elongation at Break | 7.0 % | 7.0 % | |
| Tensile Modulus | 4.50 GPa | 653 ksi | |
| Charpy Impact Unnotched | 1.40 J/cm² | 6.66 ft-lb/in² | |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Vicat Softening Point | 105 °C | 221 °F |
Users viewing this material also viewed the following:
- Polycasa PS
- Radici Radilon® SLVHPL128 (dry) Nylon 6
- Ipiranga Petrochem PH 0320 Polypropylene
- Karina 924D10/349-IS White PVC Compound
- Taiwan Sheen Soon Sheenthane® AS-422 TPU for PU Adhesive
- Techmer ES HiFill® PA6/6 GF30 HR HS BK 30% Glass Filled
- A. Schulman PP 1692 Polypropylene High Impact Copolymer
- A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene
- Eagle Brass 102 OF COPPER (Non-Certified), Hard
- Asahi Glass Fluon® PB2015 15% Graphite, PTFE Filled Compound
Copyright © lookpolymers.com All Rights Reserved