- DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66 (Unverified Data**)
DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® E41HSB is an unreinforced, high viscosity, heat stabilized polyamide 66 for injection molding and extrusion.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 84.0 MPa @Temperature 23.0 °C |
12200 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 50 % @Temperature 23.0 °C |
50 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 | |
| Elongation at Yield | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 26 % @Temperature 23.0 °C |
26 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Forms | Pellets | DAM |
| Generic | PA66 | DAM |
| Material Status | Preliminary Data | DAM |
| Processing Method | Extrusion | DAM |
| Injection Molding | DAM | |
| Product Category | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Osprey Metals 420/MA Stainless Steel Powder (Grade 95% - 16)
- SABIC Innovative Plastics Lexan® HP6NR PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® ML1665 PC
- DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**)
- A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene
- Clariant Renol PPSP0017 Polypropylene, Static Dissipative
- American Computer Optics UV Protection Glass 2 mm
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Soft Clay
- PSM Industries PolyAlloys MIM-Fe-50%Ni Grade 2 Soft Magnetic Steel
Copyright © lookpolymers.com All Rights Reserved