| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® NH-0825 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 64.7 MPa | 9380 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm @Thickness 3.17 mm |
4.04 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm |
172 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 88.0 °C | 190 °F | B/50; ISO R306 |
| Flammability, UL94 | V-2 @Thickness 0.750 - 3.00 mm |
V-2 @Thickness 0.0295 - 0.118 in |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-80 General Purpose Acrylic Resin
- RheTech Products E204-01 High Density Polyethylene, Black
- Polykemi AB POLYsan FL100 F20 SAN, Glass Fiber-Reinforced
- Parker Chomerics COMBO® Gaskets Wire Mesh EMI Gasket Selection Guide
- Kazanorgsintez 107-277 Low Density Polyethylene Composition with Improved Processibility
- Lehmann & Voss LUVOCOM® 65-8347/RD PP-copolymer, with carbon fiber
- Intercontinental Polymers Deniers 40 Polyester Staple Fiber, Deniers 40
- Ipiranga Petrochem LB 0117 LLDP
- Lehmann & Voss LUVOCOM® 80-7919 Polyacetal-copolymer, with PTFE, easy flowing
- Alliance Polymers Viprene™ G55A-32U-BLK Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved