DuPont Performance Polymers Zytel® 70G25HSLR NC010 Nylon 66 (Unverified Data**)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Zytel® 70G25HSLR NC010 Nylon 66 (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Zytel® 70G25HSLR NC010 is a 25% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in³	DAM; ISO 1183
Filler Content	25 %	25 %	DAM
Water Absorption	2.0 % @Temperature 23.0 °C	2.0 % @Temperature 73.4 °F	Equilibrium 50%RH; DAM; ISO 62, Similar to
	6.4 % @Temperature 23.0 °C	6.4 % @Temperature 73.4 °F	Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Thickness 2.00 mm	0.0030 in/in @Thickness 0.0787 in	DAM; ISO 294-4
Linear Mold Shrinkage, Transverse	0.011 cm/cm @Thickness 2.00 mm	0.011 in/in @Thickness 0.0787 in	DAM; ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	120 MPa @Temperature 23.0 °C	17400 psi @Temperature 73.4 °F	50%RH; ISO 527
	180 MPa @Temperature 23.0 °C	26100 psi @Temperature 73.4 °F	DAM; ISO 527
Elongation at Break	3.0 % @Temperature 23.0 °C	3.0 % @Temperature 73.4 °F	DAM; ISO 527
	7.0 % @Temperature 23.0 °C	7.0 % @Temperature 73.4 °F	50%RH; ISO 527
Tensile Modulus	6.10 GPa @Temperature 23.0 °C	885 ksi @Temperature 73.4 °F	50%RH; ISO 527
	8.40 GPa @Temperature 23.0 °C	1220 ksi @Temperature 73.4 °F	DAM; ISO 527
Charpy Impact Unnotched	4.50 J/cm² @Temperature -30.0 °C	21.4 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eU
	6.00 J/cm² @Temperature 23.0 °C	28.6 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 179/1eU
	6.00 J/cm² @Temperature -30.0 °C	28.6 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eU
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 179/1eA
	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	50%RH; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ASTM E 831
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	112 µm/m-°C @Temperature 23.0 - 55.0 °C	62.2 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ISO 11359-1/-2
	112 µm/m-°C @Temperature 23.0 - 55.0 °C	62.2 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ASTM E 831
Melting Point	262 °C	504 °F	10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	261 °C	502 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	252 °C	486 °F	DAM; ISO 75-1/-2
Glass Transition Temp, Tg	80.0 °C	176 °F	10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical	105 °C @Thickness 0.710 mm	221 °F @Thickness 0.0280 in	DAM; UL 746B
	120 °C @Thickness 1.50 mm	248 °F @Thickness 0.0591 in	DAM; UL 746B
	120 °C @Thickness 3.00 mm	248 °F @Thickness 0.118 in	DAM; UL 746B
UL RTI, Mechanical with Impact	95.0 °C @Thickness 1.50 mm	203 °F @Thickness 0.0591 in	DAM; UL 746B
	95.0 °C @Thickness 3.00 mm	203 °F @Thickness 0.118 in	DAM; UL 746B
UL RTI, Mechanical without Impact	105 °C @Thickness 1.50 mm	221 °F @Thickness 0.0591 in	DAM; UL 746B
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in	DAM; UL 746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; UL94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	DAM; UL94
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	DAM; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm @Temperature 23.0 °C	1.00e+15 ohm-cm @Temperature 73.4 °F	DAM; IEC 60093
Surface Resistance	1.00e+13 ohm @Temperature 23.0 °C	1.00e+13 ohm @Temperature 73.4 °F	50%RH; IEC 60093
Dielectric Constant	3.6 @Frequency 100 Hz, Temperature 23.0 °C	3.6 @Frequency 100 Hz, Temperature 73.4 °F	DAM; IEC 60250
Dissipation Factor	0.0070 @Frequency 100 Hz, Temperature 23.0 °C	0.0070 @Frequency 100 Hz, Temperature 73.4 °F	DAM; IEC 60250
Comparative Tracking Index	400 V @Thickness 3.20 mm, Temperature 23.0 °C	400 V @Thickness 0.126 in, Temperature 73.4 °F	DAM; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	295 °C	563 °F	DAM; Optimum
	285 - 305 °C	545 - 581 °F	DAM
Mold Temperature	70.0 - 120 °C	158 - 248 °F	DAM
	100 °C	212 °F	DAM; optimum
Drying Temperature	80.0 °C	176 °F	DAM
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	DAM
Moisture Content	<= 0.20 %	<= 0.20 %	DAM

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer	DAM
	Hydrolysis Resistant	DAM
Appearance	Natural Color	DAM
Drying Recommended	Yes, if moisture content of resin exceeds recommended level	DAM
Features	Antifreeze Resistant	DAM
	Chemical Resistance, Good	DAM
	Fatigue Resistant	DAM
	Fuel Resistant	DAM
	Grease Resistant	DAM
	Heat Aging Resistance, Good	DAM
	Hydrolysis Resistant	DAM
	Lubricated	DAM
	Oil Resistant	DAM
	Thermal Aging Resistance, Good	DAM
Filler	Glass fiber reinforcement	DAM
Forms	Pellets	DAM
Generic	Nylon 66	DAM
Material Status	Current	DAM
Part Marking Code	>PA66-GF25<	ISO 11469; DAM
Polymer Family	Polyamide	DAM
Polymer Type	PA66	DAM
Processing Method	Injection Molding	DAM
Product Category	Glass Reinforced Resins	DAM
	Hydrolysis Resistant Resins	DAM
Region Available - Global	Yes	DAM
Resin Identification	PA66-GF25	ISO 1043; DAM
RoHS Compliance	Contact Manufacturer	DAM
Uses	Appliance Components	DAM
	Automotive Applications	DAM
	Electrical/Electronic Applications	DAM
	Industrial Applications	DAM