PolyOne Geon™ Vinyl Wire & Cable W1100 Polyvinyl Chloride, Flexible (PVC, Flexible)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Vinyl Wire & Cable W1100 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D792
Deformation	25 % @Temperature 121 °C, Time 3600 sec	25 % @Temperature 250 °F, Time 1.00 hour	500 g; UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	47	47	15 sec; ASTM D2240
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	250 %	250 %	Type IV, 510 mm/min; ASTM D638
Tensile Modulus	0.0117 GPa	1.70 ksi	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	75.0 °C	167 °F	UL Temperature Rating
	90.0 °C	194 °F	UL Temperature Rating
Oxygen Index	27 % @Thickness 1.91 mm	27 % @Thickness 0.0752 in	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.50e+12 ohm-cm	1.50e+12 ohm-cm	ASTM D257
Dissipation Factor	0.090 @Frequency 1000 Hz	0.090 @Frequency 1000 Hz	ASTM D150

Processing Properties	Metric	English	Comments
Melt Temperature	188 - 193 °C	370 - 379 °F

Descriptive Properties	Value	Comments
Additive	Lead Stabilizer
Agency Ratings	UL QMTT2
Appearance	Black
	Dark Grey
Change in Ultimate Elongation	-25%	ASTM D543; 60°C, 1440 hr, in ASTM #2 Oil; 0.075 in
Features	Flame Retardant
	Sunlight Resistant (300 hours)
Forms	Pellets
Generic Material	PVC, Flexible
Generic Name	Polyvinyl Chloride, Flexible (PVC, Flexible)
Processing Method	Extrusion Coating
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Retention of Tensile Elongation	70%	113°C, 1.91 mm; 168 hr, UL Standard
	90%	100°C, 1.91 mm; 168 hr, UL Standard
Uses	Building Wire Insulation
	Building Wire Jacketing
	Flexible Cord Insulation
	Flexible Cord Jacketing
	Wire & Cable Applications
Wire Types	NMB
	THW
	TW