Clariant Renol R66G13HSL Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Economy
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol R66G13HSL Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Economy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Yield | 2.75 % | 2.75 % | ASTM D638 |
| Flexural Yield Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 4.31 GPa | 625 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 22.8 °C |
0.600 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture level is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- NYCOA 1838 Copolymer Nylon Alloy
- Northstar Polymers MSS-A70GQ High Performance Polyurethane Cast Elastomer System 70A
- Karina E 828-48/27-Y-RT Black PVC Compound
- Shandong Guangyin Special Resin for Badminton
- ExxonMobil Teresstic 46
- E-Polymers TEKAMID® TA210GR , 33% Glass Fiber Reinforced PA66, DAM
- BASF Paliotol™ Yellow L 2140 Color Additive
- Addiplast Addilene H 210 Polypropylene Homopolymer
- Styron Magnum™ 3490 ABS, High Gloss
Copyright © lookpolymers.com All Rights Reserved