Cossa Polimeri ESTADIENE 1030 HT V0 Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTADIENE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTADIENE 1030 HT V0 Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile Butadiene StyreneFlame retardant class V0, PBDE free, high thermal resistance, good light resistance, good processability and surface appearanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ASTM D 955
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
14 g/10 min

@Load 5.00 kg,
Temperature 240 °C
14 g/10 min

@Load 11.0 lb,
Temperature 464 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D 638
Tensile Strength, Yield 43.0 MPa
6240 psi
ASTM D 638
Elongation at Break 5.0 %
5.0 %
ASTM D 638
Flexural Modulus 2.50 GPa
363 ksi
ASTM D 790
Izod Impact, Notched 0.700 J/cm

@Temperature 0.000 °C
1.31 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
0.900 J/cm

@Temperature 23.0 °C
1.69 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Hot Ball Pressure Test 105 °C
221 °F
I.E.C. 335-1
Vicat Softening Point 110 °C

@Load 5.00 kg
230 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
121 °C

@Load 0.999 kg
250 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Glow Wire Test 960 °C
1760 °F
I.E.C. 695-2-1