Techmer ES ElectrablendÂ® PA6/6 CF30 BK 30% Carbon Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled , Nylon 66, Conductive
Manufacturer	Techmer ES
Trade Name	Electrablend®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES ElectrablendÂ® PA6/6 CF30 BK 30% Carbon Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: Electrically Conductive and LubricatedAppearance: BlackInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/inÂ³	ASTM D792
Water Absorption	0.48 % @Time 86400 sec	0.48 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0020 cm/cm @Thickness 3.17 mm	0.0020 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	97	97	ASTM D785
Tensile Strength, Yield	234 MPa	34000 psi	ASTM D638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	ASTM D638
Flexural Strength	345 MPa	50000 psi	ASTM D790
Flexural Modulus	0.0000193 GPa	0.00280 ksi	ASTM D790
Izod Impact, Notched	0.801 J/cm @Thickness 3.17 mm	1.50 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	6.41 J/cm @Thickness 3.17 mm	12.0 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	18.0 Âµm/m-Â°C	10.0 Âµin/in-Â°F	ASTM D696
Melting Point	263 Â°C	505 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	260 Â°C	500 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	257 Â°C	495 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Surface Resistance	100 - 200 ohm	100 - 200 ohm	ASTM D257