Lucent Polymers TPP-140 Polypropylene, Homopolymer, 40% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPP-140 Polypropylene, Homopolymer, 40% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.03 MPa | 4501 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 53.79 MPa | 7802 psi | ASTM D790 |
| Flexural Modulus | 3.586 GPa | 520.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.22 °C | 180.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 141 PC
- Ineos Nova PS 2521 Crystal Polystyrene (discontinued **)
- SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific)
- Shandong Dongyue Shenzhou New Material Co CHFM 250 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- Shuman 710H Utility Black ABS
- Styrolution PS-145D Polystyrene
- 3M 3350 HVAC Construction
- Beijing Ranger Chem PBT 403 M-G30 HF Halogen Free Flame Retarding FR PBT
- A. Schulman ComAlloy Hiloy® 261 Glass Reinforced, Modified SMA
- DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved