- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 238 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 238 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75, ASTM D648 |
|
Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66
Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for app..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
238
°C <br>@Thickness 3.20 mm
|
460
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics EXTEM UH1006 TPI Blend
High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
|
Resinoid 2205 Phenolic Molding, Cellulose Reinforced
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
|
Ravago Manufacturing Americas Hylon® N1013STL Nylon 6/6 (DAM)
(discontinued **)
Information provided by Ravago.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
238
°C <br>@Thickness 6.40 mm
|
460
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUMID SG4389B PA66+GF/MF38%
Feature: Injection Molding, PA66+GF/MF38%Application: Automotive (Fan & Shroud)CAS No. 32131-17-2, 25038-54-4, 65997-17-3 and 14807-96-6Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66
LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
238
°C <br>@Thickness 3.20 mm
|
460
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific)
LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RX05050 is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 GF33 TL10 HS 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Heat Stab..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
238
°C <br>@Thickness 3.20 mm
|
460
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66
LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1, 2 |
|
Polyplastics FR-PET® C3030FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
Information provided by PolyPlastics.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 461 °F | ASTM D648 |
|
A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 120x10x4, sp=64 mm; ISO 75/Af |
|
Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded
RFB24 is a Glass Bead and Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as Staramide 66 2010VK Z3)Information provided by Polymer Technology & Services, the North American..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
|
Ashley Polymers Ashlene® 525-33G Nylon 66, 33% Glass Reinforced
High impact Nylon 66 reinforced with 33% glass fibers, lubricated.Data provided by the manufacturer
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
|
Ashley Polymers Ashlene® 520-25G Nylon 66, 25% Glass Reinforced
Nylon 66, 25% glass reinforced.Data provided by the manufacturer
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 461 °F | ASTM D648 |
|
A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1,-2 |
|
Gromax CFG45-RN13N1 Nylon 6 46% Glass Filled (Dry)
Information provided by Gromax Enterprises Corp.
|
|||