- Clariant Renol PA2SP0009HW Nylon 6, Heavyweight Compound
Clariant Renol PA2SP0009HW Nylon 6, Heavyweight Compound
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA2SP0009HW Nylon 6, Heavyweight Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 8.00 g/cc | 8.00 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 22.8 °C |
0.800 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- MV Labs ER100 Er(C2H3O2)3·xH2O Erbium acetate hydrate
- Arlon 0.015" (0.381 mm) Semi-Cured Silicone Traction Motor Insulation with Fiberglass Substrate (51224R015) &n
- Saint-Gobain Tygon® LP 1600 Low Permeation Fuel Tubing
- Teknor Apex Sinvicomp SPF 3520 Polyvinyl Chloride, Flexible
- DSM Stanyl® 46HF5040 (COND) Nylon 46 40% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow (North America)
- Eurostar Starflam PK0049 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded
- C.O.I.M. LARIPUR® LPR5725 Special Adipate Ester Polyurethane
- BASF Ultramid® BG50XFI PA6 (Conditioned)
- A.D. Compound Adene NCTA Homopolymer 50% CaCO3 Filled Polypropylene
Copyright © lookpolymers.com All Rights Reserved