LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Anti-Scratch, High Impact, High FlowApplication: LCD TV Stand Base, Audio/Video HousingCAS No. 9010-94-0Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Water Absorption 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
 0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 22 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 22 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength, Yield 49.0 MPa

@Thickness 3.20 mm
 7110 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
 30 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 6.0 %

@Thickness 3.20 mm
 >= 6.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 82.4 MPa

@Thickness 3.20 mm
 11900 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.89 GPa

@Thickness 3.20 mm
 420 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 1.77 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 3.31 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.77 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 3.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.981 J/cm

@Thickness 6.40 mm,
Temperature -20.0 °C
 1.84 ft-lb/in

@Thickness 0.252 in,
Temperature -4.00 °F
 ASTM D256
0.981 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
 1.84 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 6.40 mm
 189 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
91.0 °C

@Thickness 6.40 mm
 196 °F

@Thickness 0.252 in
 ASTM D648
91.0 °C

@Thickness 3.20 mm
 196 °F

@Thickness 0.126 in
 ASTM D648
Flammability, UL94 HB

@Thickness >=1.60 mm
 HB

@Thickness >=0.0630 in
HB

@Thickness >=3.20 mm
 HB

@Thickness >=0.126 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding