- Barlog Plastics KEBAFORM C 906 LF POM Copolymer unreinforced, improved wear and friction
Barlog Plastics KEBAFORM C 906 LF POM Copolymer unreinforced, improved wear and friction
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 906 LF POM Copolymer unreinforced, improved wear and friction.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POMInformation provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ISO 527-1 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527-1 |
| Tensile Modulus | 2.15 GPa | 312 ksi | ISO 527-1 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | IEC 60243-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM |
Users viewing this material also viewed the following:
- Ineos H11G-00 Polypropylene Homopolymer
- Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (496°C - 4 hours - air cooling)
- Lubrizol Advanced Materials Pearlstick® 48-60/25 Linear Thermoplastic Polyurethane Elastomer
- Techmer ES HiFill® PA6 GF33 L UV 33% Glass Filled
- Styrolution PS 5600/5601 HIPS
- Techmer ES Elastoblend® PA6/66 IM3 BK
- Solvay TECHNYL® 27010ST PA66, Conditioned
- Polyplastics Duranex® 330HR Polybutylene Terephthalate (PBT), Hydrolysis resistant, Heat shock resistant, 30% GF filled
- Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved