Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 % @Time 86400 sec |
1.3 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ISO 2039 |
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 |
| Elongation at Break | 5.3 % | 5.3 % | ISO 527-1/-2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1/-2 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+11 ohm-cm | 7.00e+11 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 40.2 kV/mm @Thickness 1.00 mm |
1020 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF40 - PA66 Nylon 66, 40% Long Carbon Fiber Reinforced
- Petroquimica Triunfo Trilene® TS 8058 LLDPE-C6 and LDPE Blend
- DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**)
- Iran Petrochemical (PCC) PC 0104 Polycarbonate
- Mid-Mountain Materials THERMOSEAL® FIBERPAK® T22 Tamping Mix
- Styron MAGNUMâ„¢ 342 EZ Acrylonitrile Butadiene Styrene (ABS) Resin
- Eurotec® Tecomid® NB40 GR30 NL PA 6 30% glass fiber reinforced
- Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness)
- DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
- ExxonMobil Mobil Clean 10W-40 High Mileage
Copyright © lookpolymers.com All Rights Reserved