Clariant Renol BRU0000BN-182 Nylon 66, Lubricated, Nucleated, Weather Resistant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol BRU0000BN-182 Nylon 66, Lubricated, Nucleated, Weather Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 - 0.017 cm/cm | 0.012 - 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.3 MPa | 10200 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Flexural Yield Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.1 °C | 178 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PD 2201 Polypropylene, Unspecified (PP, Unspecified)
- Parker Chomerics CHO-BOND 584-29 Conductive Adhesive
- Ravago Manufacturing Americas Hylex® P1010G40FRMA Polycarbonate, 40% Glass Filled
- Phillips 66 COPYLENE® CR750CL-02 Polypropylene, Random Copolymer, NX-8000 based
- PolyOne Geon™ Vinyl Flexible XV3856 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Tipco Tipcolite® TEL 211 Phenolic Compound, Glass & Nylon Fibers, Soft Flow & Low Shrinkage
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
- Beijing Evergrow Resources TBMH-1 Glass Fiber Tissue
- ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets (discontinued **)
- DuPont Performance Polymers Zytel® 70G33HS1L BK031 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved