SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
| 67.0 MPa | 9720 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.81 GPa | 698 ksi | 1 mm/min; ISO 527 |
| 5.02 GPa | 728 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 95.0 MPa | 13800 psi | ISO 178 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.12 GPa | 598 ksi | 2 mm/min; ISO 178 |
| 4.18 GPa | 606 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.81 J/cm | 7.14 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 159 °C @Thickness 3.20 mm |
318 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® CP 1315 (discontinued **)
- Kazanorgsintez Oleox-5
- Huntsman Euredur 43 Cycloaliphatic Amine
- Mateck Magnesium Fluoride (MgF2)
- Greene Tweed ARâ„¢ 1 Abrasive-Resistant Thermoplastic
- Lord Adhesives Metech 3502 Palladium Silver Conductor Composition
- DSM Arnitel® PM471 Polyether Ester Elastomer (European and Asian Grade)
- BCC Products BC 5105 Epoxy Laminating System
- Arlon 55149R062 Silicone Rubber/Fiberglass Laminate
- Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved