Clariant Renol 612-01L Nylon 612, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 612-01L Nylon 612, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 0.00 % | 0.00 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 75 % | 75 % | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C |
0.700 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.517 MPa | 25.0 - 75.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **)
- LNP Thermocomp® EC-1006 Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Ineos ABS Centrex® 485 ASA+AES Blend (discontinued **)
- Stanelco Bioplast® GF 106 Biodegradable Plastic
- Samyang Triloy® 130 PC/PBT alloy
- Chengdu Polyster H9275Y Thermoplastic Polyether-ester Elastomer (TPEE)
- Covestro Makrolon® 8315 Polycarbonate, 10% Glass Filled
- ExxonMobil Escorene™ FL 00212 Ethylene Vinyl Acetate Copolymer (European Grade)
- Cytec (Conap) RN-1210 / EA-028 Conapoxy® Resin / Conacure® Hardener
- Beijing Ranger Chem SM-602RX70 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved