Saint-Gobain Rulon® 1410 Grade Bearing/Seal PTFE
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Saint-Gobain Perfomance Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Saint-Gobain Rulon® 1410 Grade Bearing/Seal PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of friction, and excellent abrasion and corrosion resistance while running without lubrication. They are used in bearing and seal applications from temperature extremes of 400°F to over 500°F with and without additional lubricants. A unique property of Rulon® is the absence of stick slip, that is, erratic low-speed motion. PTFE = polytetrafluoroethylene1410 Grade Bearing/Seal PTFE: A standard material for compressor piston flip seals. Gold in color. Material has thermal and electrical insulating properties. Suitable for use in steam, wet, dry, or vacuum environments. Rc 25 or higher steel mating surface.Information provided by Saint Gobain Performance Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.20 g/cc | 0.0795 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 14.8 MPa | 2150 psi | ASTM D638 |
| Elongation at Break | 210 % | 210 % | ASTM D638 |
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Coefficient of Friction, Dynamic | 0.10 - 0.20 | 0.10 - 0.20 | Dry vs. Steel |
| Coefficient of Friction, Static | 0.10 - 0.20 | 0.10 - 0.20 | Dry vs. Steel |
| Limiting Pressure Velocity | 0.263 MPa-m/sec | 7500 psi-ft/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 128 µm/m-°C @Temperature 25.6 - 93.3 °C |
71.0 µin/in-°F @Temperature 78.0 - 200 °F |
Length |
| 135 µm/m-°C @Temperature 25.6 - 149 °C |
75.0 µin/in-°F @Temperature 78.0 - 300 °F |
Length | |
| 155 µm/m-°C @Temperature 25.6 - 260 °C |
86.0 µin/in-°F @Temperature 78.0 - 500 °F |
Length | |
| CTE, linear, Transverse to Flow | 128 µm/m-°C @Temperature 25.6 - 93.3 °C |
71.0 µin/in-°F @Temperature 78.0 - 200 °F |
Diameter |
| 135 µm/m-°C @Temperature 25.6 - 149 °C |
75.0 µin/in-°F @Temperature 78.0 - 300 °F |
Diameter | |
| 155 µm/m-°C @Temperature 25.6 - 260 °C |
86.0 µin/in-°F @Temperature 78.0 - 500 °F |
Diameter | |
| Thermal Conductivity | 0.259 W/m-K | 1.80 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Minimum Service Temperature, Air | -240 °C | -400 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gold |
Users viewing this material also viewed the following:
- Ovation Polymers SOFTAPLAS™ S 56A Thermoplastic Elastomer
- Lubriplate SFL-2 Aluminum Complex Synthetic Food Machinery Grade Grease
- Multibase Multibatch® ME 50009 Anti-blocking Masterbatch
- Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables
- Borealis HG265FB Polypropylene
- DSM Biomedical Elasthane™ 55D Thermoplastic Polyether Polyurethane (TPU)
- Clariant Renol PCSP0006 Polycarbonate, Laser Markable
- ATI Allvac® Ti-17 Titanium Alloy, Heat Treatment: 899°C (1650°F) + Age
- Aremco HiE-Coat™ 840-MS High Emissivity Silicone-Ceramic Coating
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 718°C (1325°F)/8hr/AC to 621°C (1150°F)/8hr/AC
Copyright © lookpolymers.com All Rights Reserved