Solvay TECHNYL® B 238 Black 21 N PA66/6, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® B 238 Black 21 N PA66/6, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced and modified copolyamide 66/6, heat stabilized, with improved impact resistance, for injection molding.Available in: EuropeProduct Applications: TECHNYL B 238 is particularly recommended for applications where high thermal stress rates and good impact resistance are required, also for parts which could break during assembly or parts used at low humidity level. This grade is commonly used in: automotive industry for under bonnet fasteners. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183/A
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ISO 527 Type 1A
Tensile Strength, Yield 40.0 MPa
5800 psi
ISO 527 type 1 A
Elongation at Break 250 %
250 %
ISO 527 Type 1A
Elongation at Yield 12 %
12 %
ISO 527 type 1 A
Tensile Modulus 0.900 GPa
131 ksi
ISO 527 Type 1A
Flexural Strength 27.0 MPa
3920 psi
ISO 178
Flexural Modulus 0.700 GPa
102 ksi
ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/1eA
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.070
0.070
IEC 60250
Comparative Tracking Index 500 V
500 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Moisture Content <= 0.20 %
<= 0.20 %