SABIC Innovative Plastics Xenoy® XD1588 PBT+PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® XD1588 PBT+PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT+PC blend for painted automotive exterior applications, having good flow.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 18 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 18 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 81.0 MPa
11700 psi
ISO 2039-1
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
50 mm/min; ISO 527
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Yield Strength 65.0 MPa
9430 psi
2 mm/min; ISO 178
Flexural Modulus 1.90 GPa
276 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 55.0 kJ/m²
26.2 ft-lb/in²
80*10*4; ISO 180/1A
28.0 kJ/m²

@Temperature -40.0 °C
 13.3 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/2C
5.50 J/cm²
26.2 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Taber Abrasion, mg/1000 Cycles 30
30
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Thermal Conductivity 0.180 W/m-K
1.25 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 122 °C
252 °F
Rate B/50; ISO 306
125 °C
257 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
 3.1

@Frequency 1.00e+6 Hz
 IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
 3.3

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
 0.0020

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2