Clariant 612-01 HSL Black Nylon 612, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant 612-01 HSL Black Nylon 612, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 0.00 % | 0.00 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 75 % | 75 % | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C |
0.700 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 254 - 271 °C | 490 - 520 °F | |
| Melt Temperature | 249 - 266 °C | 480 - 510 °F | |
| Mold Temperature | 79.4 - 121 °C | 175 - 250 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content of 0.2% or less |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.517 MPa | 75.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Zytel® 101L BKB009 Nylon 66 (Unverified Data**)
- MarkeTech Repton 115 Aluminum Oxide
- LG Chemical Lupox® SG5300 PBT+PET+GF30%
- LG Chemical Lupoy 1301V-10 Polycarbonate Resin
- Gromax BFG45-B100N1 Nylon 6 46% Glass Filled (Conditioned)
- Saint-Gobain Normount® V1300 White Polyurethane Foam Bonding Tape for Interior Use
- Teknor Apex Sinpolene TPP1010 Polypropylene
- Tipco Clearbatch - 10 Clarifying & Nucleating Masterbatch
- Hexcel® HexWeb® CR-PAA™ 1/4-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- ExxonMobil LD 317.87 Film Resin
Copyright © lookpolymers.com All Rights Reserved