Tra-Con Tra-Bond 2106 Fast Cure, Medium Viscosity Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond 2106 Fast Cure, Medium Viscosity Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND 2106 is an exceptional epoxy formulation recommended for lower temperature or wet industrial bonding applications where FAST CURING is required. This clear, two-part, medium viscosity system mixes easily at room temperature, contains no solvents, and is suitable for high performance structural bonding applications where the combination of very fast room temperature cure coupled with low shrinkage and excellent mechanical and electrical properties is required. It develops strong, tough bonds to metals, phenolic plastics, polyesters, glass and glass fabtics, hardboards and forestry products, ceramics, rubber, masonry materials, and other construction materials. Fully cured TRA-BOND 2106 is an excellent electrical insulator, and provides superior resistance to vapors and gases, water, galvanic action, petroleum fuels, salt solutions, and many other organic and inorganic compounds. Note: TRA-BOND 2106 develops a high exotherm. Use immediately after mixing. The exothermic reaction begins within 2 minutes after initiating the mixing step, so have everything ready before removing BIPAX clamp.Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
Mixed
Viscosity 15500 cP

@Temperature 25.0 °C
15500 cP

@Temperature 77.0 °F
After mixing
Mechanical Properties Metric English Comments
Hardness, Shore D 25
25
10 min @ 25°C
67
67
30 min @ 25°C
72
72
60 min @ 25°C
Izod Impact, Notched 1.01 J/cm
1.90 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 115 °C
239 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Glass Transition Temp, Tg 32.0 °C
89.6 °F
Ultimate Tg
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+11 ohm-cm
5.00e+11 ohm-cm
Dielectric Constant 4.8

@Frequency 1000 Hz
4.8

@Frequency 1000 Hz
Dielectric Strength 16.1 kV/mm
410 kV/in
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 65.0 °C
1.00 hour

@Temperature 149 °F
240 - 360 min

@Temperature 25.0 °C
4.00 - 6.00 hour

@Temperature 77.0 °F
Pot Life 5.0 min
5.0 min
Descriptive Properties Value Comments
Color Transparent, Straw
Mix Ratio, parts by weight 100/93
Resin/Hardener