- BASF Ultramid® A3HG6 HR BK 23591 30% Glass Filled PA66 (Dry)
BASF Ultramid® A3HG6 HR BK 23591 30% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3HG6 HR BK 23591 30% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 30% glass-fiber reinforced injection-molding grade with enhanced hydrolysis resistance, e.g., for applications in vehicle cooling systems.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 5.2 - 5.8 % | 5.2 - 5.8 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 - 1.9 % | 1.5 - 1.9 % | 23°C; 50% RH; ISO 62 |
| 1.7 % | 1.7 % | 50% RH; ISO 62 | |
| 5.5 % | 5.5 % | Saturation; ISO 62 | |
| Viscosity Measurement | 145 | 145 | ISO 307 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | restricted |
| Melt Flow | 34.25 g/10 min @Load 5.00 kg, Temperature 275 °C |
34.25 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 225 MPa | 32600 psi | ISO 2039-1 |
| Tensile Strength, Yield | 190 MPa @Temperature 23.0 °C |
27600 psi @Temperature 73.4 °F |
50 mm/min; ISO 527-1/-2 |
| 240 MPa @Temperature -40.0 °C |
34800 psi @Temperature -40.0 °F |
ISO 527 | |
| Elongation at Yield | 3.2 % | 3.2 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | ISO 527-1/-2 |
| Flexural Strength | 275 MPa | 39900 psi | at max force; ISO 178 |
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 - 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 16.7 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 260 °C | 500 °F | DIN 53765 |
| Maximum Service Temperature, Air | 240 °C | 464 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Decomposition Temperature | >= 310 °C | >= 590 °F | |
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
746B |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
746B |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
| Dielectric Constant | 3.5 @Frequency 1.00 Hz |
3.5 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.014 @Frequency 100 Hz |
0.014 @Frequency 100 Hz |
IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 290 °C | 554 °F | Feed zone |
| Zone 2 | 290 °C | 554 °F | Compression |
| Zone 3 | 290 °C | 554 °F | Metering-zone |
| Zone 4 | 290 °C | 554 °F | Nozzle |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion |
| 290 °C | 554 °F | Optimal | |
| Mold Temperature | 80.0 °C | 176 °F | Optimal |
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal |
| <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 23591 | |
| Commercial Status | Europe and North America | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3857CT TPE, PP Overmold or Standalone use
- Polykemi AB POLYabs H00 HF ABS, Heat Resistant, High Flow
- Albis Plastics Tedur® L 9512 PPS, 45% Glass Fiber (discontinued **)
- Lushan VB517 Adhesive Resin for Aluminum-Plastic Composite Panel (ACP), High Temperature
- Saint-Gobain CHR® SG33-05(R) Industrial Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Eagle Brass 230 Red Brass, 1/2 Hard
- Constellium PLAN OX 5754 Aluminum Rolled Plate
- Plaskolite Optix® CP - 75 HID General Purpose Acrylic Resin
- Borealis Supercure™ LS4201S Polyethylene Insulation Compound, Crosslinkable