SABIC Innovative Plastics Xenoy® ENH2900 PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® ENH2900 PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applications
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 26 g/10 min

@Load 5.00 kg,
Temperature 266 °C
26 g/10 min

@Load 11.0 lb,
Temperature 511 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 65 %
65 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.48 GPa
360 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 89.0 MPa
12900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.50 J/cm
10.3 ft-lb/in
ASTM D256
Dart Drop, Total Energy 65.0 J

@Temperature 23.0 °C
47.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C

@Thickness 3.20 mm
172 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 102 °C
216 °F
Rate B/50; ASTM D1525
Flammability, UL94 V-1

@Thickness 1.10 mm
V-1

@Thickness 0.0433 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 2.50 mm
5VB

@Thickness 0.0984 in
UL 94