Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH GF1030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH GF3030 PD2 PP, Glass Fiber-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-1/-2 |
DSM Akulon® K223-HMS6 Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
LATI Latilon 28D K/40 PC, 40% Carbon Fiber Reinforced Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided b.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
LATI Latilub 87/28-12T G/20 PC, 20% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polycarbonate (PC). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP STAT-KON DEL329EP PC (Europe-Africa-Middle East) LNP* STATKON* DEL329EP is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features include: Electrically Conductive, Internally Lubricated, Flame retard.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP STAT-KON DX04489C PC LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
SABIC Innovative Plastics Xenoy® 6370 PBT+PC (Europe-Africa-Middle East) XENOY 6370 is an impact modified semi-crystalline thermoplastic. blend with 30% glass fibre reinforcement offering toughness and ductility. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC LNP* THERMOCOMP* DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC (Europe-Africa-Middle East) LNP* Thermocomp* DF008ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Infino® LS-3302 PC, 30% Glass Filled High Impact High-impact resistant PC/GF with 30% GF reinforcement for camera body tubeInformation provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | 0.157 in, annealed; ASTM D648 |
Styron EMERGEâ„¢ 4330-15 Polycarbonate EMERGEâ„¢ PC 4330-15 advanced resin is a polycarbonate resin offering ultraviolet light stability, high heat resistance and maximum toughness. Applications: Consumer Electronics and Information.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific) Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Annealed; ISO 75-2/A |
Styron CALIBREâ„¢ 303-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300-115 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East) NORYL CTI2550 is a glass/mineral filled material with a Vicat B/120 of 160 °C according ISO 306. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL GFN3L PPE+HIPS (Asia Pacific) PPE+PS, GF30%, hydrolytic stability improved |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1080 Glass Fiber-Reinforced Homopolymer Polypropylene DescriptionPolyfort® FPP 1080 is a 20% fiber-reinforced homopolymer polypropylene with excellent strength and heat resistance. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3710 is a 45% glass filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | DIN 53461 |
Polyram RamOfin PPH307G6 Polypropylene, 30% Glass Fiber 30% glass fiber reinforced, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | unannealed; ISO 75 |
Chi Mei Wonderlite® PC-175 Polycarbonate Optical Disk |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
Eurotec® Tecotek® PC43 GR20 BK002 PC, 20% glass fiber reinforced, black Information provided by Eurotec® |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
Eurotec® Tecotek® PC43 GR30 BK002 PC, 30% glass fiber reinforced, black Information provided by Eurotec® |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-2/AF |
Addiplast Addinyl B2 ZM30 Nylon 6, 30% Mineral Filled Mineral filled, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
Asahi Kasei Xyron® 740V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75-2 |
CENTROPLAST CENTROLEN PP GF 30 Polypropylene 30% glass fiber This material is a low density, easily machined plastic that has high impact resistance and dimensional stability. Applications include air filter housings, fan blades, and fittings with high loads... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
GEHR Plastics PPE-30GF Polyphenylene Ether, 30% Glass Fiber
(discontinued **) The 30% glass fiber reinforced PPE has an improved dimensional stability, a very high stiffness and heat resistance that allows further uses. |