Polyram RamOfin PPH307G6 Polypropylene, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH307G6 Polypropylene, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM-D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM-D638 |
| Tensile Modulus | 5.30 GPa | 769 ksi | ASTM-D790 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.40 J/cm @Temperature 23.0 °C |
2.62 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SHRINK® Heat Shrink EMI Shielding
- Pau Tai UNISTAB WP-148 Solid Complex Stabilizer
- PolyOne Geon™ Vinyl Flexible B80MB Polyvinyl Chloride, Flexible (PVC, Flexible)
- LG Chemical MI-730 MIPS
- Shandong Dongyue Shenzhou New Material Co DS2604 Fluoroelastomer Copolymer Gum
- A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene
- ExxonMobil LD 051.LQ Shrink Film Resin
- ConocoPhillips 220 Gear Oil AGMA Lubricant No. 5 EP
- Eurostar Staramide BG3 PA6, 15% Glass Filled, Injection Molded
- Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal
Copyright © lookpolymers.com All Rights Reserved