SABIC Innovative Plastics LNP STAT-KON DEL329EP PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL329EP PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STATKON* DEL329EP is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features include: Electrically Conductive, Internally Lubricated, Flame retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 0.22 % @Time 86400 sec |
0.22 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 8.60 GPa | 1250 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 143 MPa | 20700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
45.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7321 BLK
- Polykemi AB POLYshine PBT D221 PBT, Impact Modified
- Heatbath/Park Alu-Braze 860 Aluminum Brazing Salt
- STAR Thermoplastic Alloys & Rubbers StarXTRUDE XTR-95-1000 TPE
- Saint-Gobain COHRlastic® CF3320 Reinforced Solid Rubber
- Silberline Silvet® 210-20-J
- Samsung Cheil Industries Starex® VC-0830 ABS, Unreinforced FR
- A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene
- Dow ATTANE™ 4404G, 0.8mil Ultra Low Density Ethylene/Octene Copolymer
- LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved