- SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC
SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 114 MPa | 16500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 7.5 % | 7.5 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.63 GPa | 1250 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 149 MPa | 21600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 185 MPa | 26800 psi | ISO 178 | |
| Flexural Modulus | 7.86 GPa | 1140 ksi | 2 mm/min; ISO 178 |
| 8.23 GPa | 1190 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.14 J/cm | 17.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Okulen® 1000 - REG PE Multicoloured fine
- Lubriplate SFGO Ultra-46 PAO-Based Synthetic Food Machinery Grade Fluid
- Schwartz Technical Plastics LAMIGAMID® 324 Cast Polyamide 6, MoS2, Heat Stabilized, Dry
- Shakespeare WonderThread® SN-38 High tenacity TEX# 60 Nylon Industrial Sewing Thread
- Teknor Apex Monprene® MP-1838-R Thermoplastic Elastomer
- Hexcel® HexPly® F522 Epoxy Resin, W3C282 Carbon Fabric
- Covestro Makrolon® 6385 Polycarbonate, Injection Grade
- BASF Lupranate® MP102 Isocyanate Modified MDI
Copyright © lookpolymers.com All Rights Reserved