LATI Latilub 87/28-12T G/20 PC, 20% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass + PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 87/28-12T G/20 PC, 20% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polycarbonate (PC). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0065 cm/cm
0.0045 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 5.70 GPa
827 ksi
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Coefficient of Friction, Dynamic 0.20
0.20
Coefficient of Friction, Static 0.26
0.26
K (wear) Factor 15.0 x 10-8 mm³/N-M
7.45 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Vicat Softening Point 150 °C

@Load 5.00 kg
302 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
V-1

@Thickness 3.00 mm
V-1

@Thickness 0.118 in
Processing Properties Metric English Comments
Melt Temperature 275 - 320 °C
527 - 608 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa