- A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene
A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 3710 is a 45% glass filled homopolymer polypropylene product. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs PB600 PbI2 Lead(II) iodide
- Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 7628 E-Glass Reinforced
- Grupo Repol Dinalon® A1S25 PA66 Unreinforced
- Lucite International Elvacite ® 3008 Acrylic Resin
- SABIC Innovative Plastics LNP THERMOCOMP DX06411 PC (Asia Pacific)
- DSM Arnite® TV4 261 PBT-30% Glass Reinforced (European and Asian Grade)
- Fainplast Compounds PHA 78 Flexible PVC, Transparent Extrusion
- Arkema Group Appryl® 7280 Polypropylene - Polyethylene Copolymer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A
- LTL Color Compounds ColorFast® FRPS100 Styrene, High Impact
Copyright © lookpolymers.com All Rights Reserved