SABIC Innovative Plastics NORYL GFN3L PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN3L PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS, GF30%, hydrolytic stability improved
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.3 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.3 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | SABIC - Japan Method |
| Elongation at Break | 8.0 - 10 % | 8.0 - 10 % | SABIC - Japan Method |
| Flexural Strength | 159 MPa | 23100 psi | ASTM D790 |
| Flexural Modulus | 7.44 GPa | 1080 ksi | ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm | 2.38 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 - 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 - 23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.93 @Frequency 50.0 - 60.0 Hz |
2.93 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
Users viewing this material also viewed the following:
- Flint Hills 11R12A Specialty Homopolymer Polypropylene
- Styrolution Polystyrol 168 N GR 2 PS
- Teknor Apex HFFR 2003 Polyolefin, Halogen Free
- SABIC Innovative Plastics NORYL N110HG PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene
- ExxonMobil Unirex N 3
- Asahi Kasei Xyron® 540V Modified Polyphenylene Ether
- Solvay Specialty Polymers Amodel® AS-1945 HS Polyphthalamide (PPA) (Unverified Data**)
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed
Copyright © lookpolymers.com All Rights Reserved