SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable water applications and brings potential faster cycle time and lower stress than other 30% glass reinforced Noryl* PPO/PS blends. Noryl* GFN1430V has been certified for potable water applications up to 85C in Europe and North America in limited colours.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| 26 g/10 min @Load 10.0 kg, Temperature 300 °C |
26 g/10 min @Load 22.0 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 |
| 8.00 GPa | 1160 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178 |
| 169 MPa | 24500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 7.10 GPa | 1030 ksi | 2 mm/min; ISO 178 |
| 7.50 GPa | 1090 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.850 J/cm @Temperature -30.0 °C |
1.59 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.920 J/cm @Temperature 23.0 °C |
1.72 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 5.20 J/cm @Temperature 23.0 °C |
9.74 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| 5.20 J/cm @Temperature -30.0 °C |
9.74 ft-lb/in @Temperature -22.0 °F |
ASTM D 4812 | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Impact Test | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 149 °C | 300 °F | Rate B/50; ASTM D 1525 | |
| 150 °C | 302 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREWHITE PP 22-50
- Lubrizol Advanced Materials Pearlbond® DAP 750/2 Thermoplastic Polyurethane
- SABIC Innovative Plastics NORYL V095 PPE+PS (Europe-Africa-Middle East)
- UBE UBEPOL BR340L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- American Elements Titanium Carbide Nanoparticles
- ExxonMobil Mobil Delvac Coolant/Antifreeze Extended Life
- Dow SE SLR-4400 Solution polymerized Styrene Butadiene Rubber (S-SBR)
- A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified
- LyondellBasell PTB Propylene glycol tertiary butyl ether
Copyright © lookpolymers.com All Rights Reserved