SABIC Innovative Plastics LNP STAT-KON DX04489C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX04489C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| Elongation at Yield | 2.2 % | 2.2 % | ASTM D638 |
| Tensile Modulus | 16.63 GPa | 2412 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 15.53 GPa | 2252 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S EF 40A-3S1964 Thermoplastic Elastomer (TPE)
- Polykemi AB POLYfill PPC K5025 PP, Mineral Reinforced
- Formosa Plastics Formolene® LH5206 Injection Molding HDPE (discontinued **)
- LyondellBasell Alathon® M6061 High Density Polyethylene, Injection Molding Grade
- Borealis Supersmooth™ LE0592S Polyethylene
- A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane
- Lubrizol ESTANE® 58300 Ether Based Thermoplastic Polyurethane (European Grade)
- DSM Akulon® S223-HM8 (Dry) 40% Mineral Reinforced, Heat Stabilized Nylon 66 (North America)
- Fainplast Compounds Ethylplus 613 HPE Polyethylene Cable Compound
- ArcelorMittal 16 High formability steel for drawing, Hot rolled
Copyright © lookpolymers.com All Rights Reserved